Description
TAURUS MIG STAINLESS STEEL WIRE GASLESS FCW 316L
TAURUS 316L-T0-3 FLUX CORE STAINLESS STEEL MIG WIRE has excellent properties including good levels of strength and corrosion resistance. This makes this wire ideal for applications in industries such as food and beverages, power plant, chemical and marine/shipbuilding. Moreover, it produces beads with an attractive, polished appearance obviating the need to apply extensive post-weld brushing. Due to its low carbon content, TAURUS 316L-T0-3 wire offer good resistance to inter-granular corrosion.
Overall this wire has the capacity to withstand the harshest environments without compromising its weld integrity and corrosive resistance. It offers enhanced performance, results in improved productivity and gives the assurance that industry standards for quality and durability productivity are met. By following proper welding procedures and guidelines, welders can harness the advantages of the TAURUS 316L-T0-3 flux-core wire to achieve reliable and effective welds in various industrial sectors.
SOME KEY FEATURES
- Suited for flat and horizontal welding positions.
- Excellent resistance to the effects of pitting and corrosion.
- Excellent arc stability.
- Wire spatter loss kept to a minimum.
- Easy flux removal.
- Polished weld bead appearance.
- Low post weld brushing.
- High deposition rate and welding speed.
WELDING POSITIONS
All welding positions
CLASSIFICATIONS
AWS A5.22 E316LT0-3
| TYPICAL COMPOSITION | % |
| Carbon | 0.03 |
| Manganese | 1.4 |
| Silicon | 0.8 |
| Chromium | 19 |
| Nickel | 12 |
| Molybdenum | 2.8 |
| Sulfur | 0.008 |
| Phosphorus | 0.02 |
| MECHANICAL PROPERTIES | AS WELDED |
| Tensile strength | 560 Mpa |
| Yield strength | 420 Mpa |
| Elongation | 37% |
| Impact Strength | 40 J |
| Test Temperature | -60°C |
AVAILABLE IN
0.9mm – 1kg / 5kg spool pack